Influence of heat treatment on the properties of the consolidated AZ91D Mg alloy chips was performed in this study. The chips were pressed into a die to form a compact with a green density of 1.6 g/cm3. The 50 mm diameter green compact was then extruded i Influence of heat treatment on the properties of the consolidated AZ91D Mg alloy chips was performed in this study. The chips were pressed into a die to form a compact with a green density of 1.6 g/cm3. The 50 mm diameter green compact was then extruded i